Mode-locked operation in thulium-holmium doped fiber laser based on Cr2AlC MAX phase SA coated arc-shaped fiber
Document Type
Article
Publication Date
3-1-2023
Abstract
This study presents the application of MAX phase material as a mode-locker in the thulium-holmium-doped fiber laser (THDFL) cavity in generating ultrashort pulses. MAX phase materials were rapidly developed for applications in the pulsed laser field due to their promising properties and characteristics, such as strong nonlinear absorption, high damage tolerance, and good thermal and electrical conductivities. Chromium Aluminum Carbide (Cr2AlC) MAX phase sample was explicitly introduced into the cavity by drop-casting the Cr2AlC onto the fabricated arc-shaped fiber. As a result, an ultrafast mode-locking laser system was achieved utilizing a Cr2AlC saturable absorber (SA) at a pump power of 115.8 mW, having a central wavelength of 1908.58 nm. The spectral bandwidth obtained was 3 nm, and a measured pulse repetition rate and pulse width of 12.14 MHz and 1.3 ps, respectively. The results indicate that Cr2AlC SA is a promising material to be used as a passive SA to initiate the mode-locking generation of fiber laser in the 1.9 mu m band.
Keywords
MAX phase, Chromium aluminum carbide, Mode-locked laser, Fiber laser, Arc-shaped fiber
Divisions
PHYSICS,photonics
Funders
Ministry of Higher Education, Malaysia [Grant No: PRC-2014],Universiti Malaya [Grant No: RK021-2019],Institut Pengurusan dan Pemantauan Penyelidikan, Universiti Malaya [Grant No: RU005-2021]
Publication Title
Optical and Quantum Electronics
Volume
55
Issue
3
Publisher
Springer
Publisher Location
VAN GODEWIJCKSTRAAT 30, 3311 GZ DORDRECHT, NETHERLANDS