The digitalisation in cobalt-chromium framework fabrication. surface roughness analysis: A pilot study
Document Type
Article
Publication Date
10-1-2021
Abstract
Selective laser melting (SLM) is a new technique in fabricating cobalt-chromium denture framework. However, the surface properties of cobalt-chromium denture framework fabricated using the aforementioned technique have not been widely investigated. The aim of this paper was to investigate the surface roughness of cobalt-chromium alloy in removable partial denture fabricated with SLM technique. Cobalt-chromium denture frameworks were fabricated with two techniques (n = 10); the conventional lost-wax casting (conventional group) and SLM techniques (SLM group). Specimens from the conventional group were subjected to the standard cobalt-chromium denture polishing protocols. No treatment was employed for specimens from the SLM group. All specimens were subjected to surface roughness measurement on polished and fitting surfaces using non-contact optical three-dimensional metrology and surface roughness analysis machine (Infinite Focus Real 3D Alicona). Statistical analysis showed no significant difference in surface roughness between the specimens from conventional and SLM groups (p > 0.05). There was no statistically significant difference in surface roughness between the polished and fitting surfaces of SLM specimens (p > 0.05). Surface roughness quality of the cobalt-chromium denture framework fabricated with the SLM technique is comparable to that fabricated with the conventional lost-wax casting technique. The surface roughness of SLM fabricated cobalt-chromium denture frameworks carries the same surface roughness quality between the polished and fitting surfaces.
Keywords
Cobalt chromium, Denture, Selective laser melting, Surface roughness
Divisions
Dentistry
Publication Title
Sains Malaysiana
Volume
50
Issue
10
Publisher
Penerbit Universiti Kebangsaan Malaysia
Publisher Location
FACULTY SCIENCE & TECHNOLOGY, BANGI, SELANGOR, 43600, MALAYSIA