Synthesis and Characterization of Chicken Bone-Derived Hydroxyapatite Incorporating Pectin
Document Type
Article
Publication Date
12-1-2023
Abstract
Hydroxyapatite (HA) was synthesized from chicken bone waste by calcination. Pectin was extracted from orange peels by microwave irradiation, and 1 and 3 wt % of pectin was incorporated into the HA. The resulting powders were then pressed into disk samples before being sintered at temperatures of 1050, 1150, and 1250 degrees C for 2 h. Various analytical techniques, including Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy, density measurement, and Vickers microhardness tests, were used to evaluate the characteristics and mechanical properties of the samples. The incorporation of pectin did not interfere with the pure phases of HA, and minimal amounts of beta-tricalcium phosphate were detected in the XRD patterns. Both ball milling and the addition of pectin effectively reduced the particle size of HA. However, the addition of pectin above 1 wt % did not contribute significantly to the densification and hardness of chicken bone-derived HA (CHA) compared with ball-milled CHA. Samples sintered at 1050 degrees C had the lowest relative density, owing to incomplete particle fusion. Increasing the sintering temperature resulted in a maximum relative density of ca. 95 % and a Vickers microhardness of 4.12 GPa for ball-milled CHA samples sintered at 1250 degrees C. Sintering temperature and ball milling were observed to play a more significant role in the densification and hardness of CHA compared with the addition of pectin.
Keywords
Bioceramics, Hardness, Hydroxyapatite, Pectin
Divisions
mechanical
Funders
TAR UMT Internal Research Grant (UC/I/G2021-00080),Tunku Abdul Rahman University of Management and Technology,Universiti Tunku Abdul Rahman
Publication Title
Chemical Engineering & Technology
Volume
46
Issue
12, SI
Publisher
Wiley
Publisher Location
POSTFACH 101161, 69451 WEINHEIM, GERMANY