The effect of heat treatment on bismuth oxyiodide thin films for lead-free perovskite solar cells
Document Type
Article
Publication Date
3-1-2023
Abstract
Lead-free bismuth oxyiodide (BiOI) perovskite solar cells (PSCs) have been successfully fabricated using successive ionic layer adsorption and reaction technique. The effect of heat treatment temperature on thickness, conductivity and microstructure of BiOI thin films has been studied prior to the device fabrication. The BiOI film morphology formed flake agglomeration like flower platelets for as deposited BiOI film. However, the agglomeration and the flakes were shattered when the BiOI was annealed above 450 degrees C. This is associated with the trend in conductivity measurement where BiOI achieved the optimum conductivity when it was heat treated at 350 degrees C and reduced as the heat treatment exceeded 450 degrees C. This could be due to the reduction of grain boundaries because of development of the flake sizes during the heat treatment, material sublimation and particle aggregations that developed higher resistance in the BiOI layers. The device performance under optimum heat treatment has been characterized using I-V measurement under a solar spectrum simulator with AM 1.5 illuminations. BiOI PSCs treated at 350 degrees C showed similar to 6% efficiency. This study provided better understanding on BiOI thin film behaviors under several heat treatments, and it has potential to be applied as lead-free PSCs.
Keywords
heat treatment, Lead-free bismuth oxyiodide, BiOI thin film behaviors
Divisions
PHYSICS
Publication Title
JOM Journal of the Minerals, Metals and Materials Society
Volume
75
Issue
3
Publisher
Springer
Publisher Location
ONE NEW YORK PLAZA, SUITE 4600, NEW YORK, NY, UNITED STATES