Structural and impedance analysis of Ba0.9925Er0.0075TiO3for microelectronic application
Document Type
Conference Item
Publication Date
7-21-2021
Abstract
The Ba0.9925Er0.9975TiO3 ceramics that were prepared via solid-state reaction route were found to be phase pure at the final sintering temperature of 1350°C. The highest value of the dielectric constant is about 9000 measured at 10Hz and decreases to about 1000 at the Curie temperature at much higher frequencies. The Ba0.9925Er0.9975TiO3 is found to be of high-K dielectric materials with properties a thousand times greater than SiO2. At room temperature application, the Ba0.9925Er0.9975TiO3 exhibits a dielectric constant value from 1000 to 2500, depending upon the frequencies. The conductivity and activation energy of the Ba0.9925Er0.9975TiO3 lies in the semiconductor region. The dielectric loss is a very low and very suitable candidate for microelectronic applications. © 2021 Author(s).
Keywords
Barium titanates, Microelectronic, Conductivity, Activation energy, Dielectric, Semiconductor
Divisions
nanotechnology
Publication Title
AIP Conference Proceedings
Volume
2347
Event Title
8th International Conference on Advanced Material Engineering and Technology, ICAMET 2020
Event Location
Langkawi
Event Dates
26 - 27 Novemver 2020
Event Type
conference