Characterization, disintegration, and dissolution analyses of carrageenan-based hard-shell capsules cross-linked with maltodextrin as a potential alternative drug delivery system
Document Type
Article
Publication Date
3-1-2020
Abstract
Hard-shell capsules commonly consist of gelatin which is not a universal material considering it is extracted from animal parts. Moreover, the mad cow disease triggered the scrutinization of the use of gelatin in pharmaceutical products. Hence, an alternative to conventional hard-shell capsules is needed. Carrageenan- (CRG-) based hard-shell capsules were successfully prepared by cross-linking CRG with maltodextrin (MD) and plasticizing with sorbitol (SOR). These CRG-MD/SOR hard-shell capsules were produced as an alternative to conventional hard-shell capsules in the oral drug delivery system (DDS). The physical properties of CRG-MD/SOR capsules were characterized using the degree of swelling, FTIR, and SEM analyses. The disintegration and dissolution profile release of paracetamol from CRG-MD/SOR hard-shell capsules was performed in an aqueous medium with three different pH levels. The degree of swelling of CRG-MD/SOR was 529.23 +/- 128.10%. The main peaks in the FTIR spectrum of CRG-MD/SOR were at 1248, 930, 847, and 805 cm(-1) for ester sulfate groups, 3,6-anhydrogalactose, galactose-4-sulfate, and 3,6-anhydrogalactose-2-sulfate, respectively. The SEM analysis exhibited minuscule pores on the surface of CRG and CRG-MD/SOR at 5000 times of magnification. The CRG-MD/SOR capsules required 18.47 +/- 0.11 min on average to disintegrate. The CRG-MD/SOR dissolution was better in a weakly acidic medium (pH 4.5) than in a strongly acidic (pH 1.2) and neutral (pH 6.8) media. Based on the aforementioned results, CRG-MD/SOR capsules are the potential candidate to replace conventional hard-shell capsules.
Keywords
Gelatin, Starch, Films
Divisions
pharmacy
Funders
Universitas Airlangga through their program entitled "Penelitian Unggulan Fakultas",Ministry of Research, Technology and Higher Education of Republic of Indonesia through the PMDSU Scholarship Program
Publication Title
International Journal of Polymer Science
Volume
2020
Publisher
Hindawi
Publisher Location
ADAM HOUSE, 3RD FLR, 1 FITZROY SQ, LONDON, W1T 5HF, ENGLAND