Abstract
Porous three-dimensional hydroxyapatite (HA) scaffolds were prepared using bovine cortical bone derived HA (BDHA). Analyses of the morphology, chemical composition, and phase purity of the scaffold were performed using scanning electron microscopy (SEM), micro-computer tomography (micro-CT), Fourier transform infrared spectroscopy (FTIR), energy dispersive X-ray spectroscopy (EDX), and X-ray diffraction (XRD). SEM images revealed the rough and porous surface of the scaffold, while micro-CT showed the average porous volume of 76.7 +/- 0.6 and pore size of 0.04-0.25 mm. Single phase corresponding to standard HA was observed using XRD, and FTIR confirmed the presence of functional groups similar to HA. The EDX analysis revealed a Ca/P ratio of 1.61, which was comparable with HA stoichiometry. Compressive strength of the BDHA scaffold was found to be 1.3 +/- 0.09 MPa. After 14 days of human bone marrow stromal cells (hBMSCs) seeding, SEM and confocal analysis revealed cell attachment to the surface and infiltration into the pores. Alamar blue and alkaline phosphatase assays showed significantly increased cell proliferation and differentiation in the BDHA scaffold, when compared with that in the monolayer (p < 0.01). In addition, quantitative real-time polymerase chain reaction (qPCR) data confirmed the up regulation of genes involved in osteogenic differentiation of mesenchymal stem cells. Our findings indicate that BDHA scaffold provides a favorable physiological environment for enhanced cell attachment, proliferation, and osteogenic differentiation of hBMSCs. (C) 2013 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Keywords
Sintering, Porosity, Hydroxyapatite, Mesenchymal stem cell, in-vitro, proliferation, degradation
Divisions
fac_med
Publication Title
Ceramics International
Volume
40
Issue
1
Publisher
Elsevier
Additional Information
ISI Document Delivery No.: AA0XK Times Cited: 1 Cited Reference Count: 22 Krishnamurithy, G. Murali, Malliga Raman Hamdi, M. Abbas, A. A. Raghavendran, Hanumantharao Balaji Kamarul, T. University of Malaya FP026/2009; HIR-MOHE The authors are grateful to the University of Malaya research Grant (FP026/2009) and HIR-MOHE for supporting this study. Elsevier sci ltd Oxford A