Abstract
In this study, Mo nanoparticles were used as a reinforcing material into the Sn-3.8Ag-0.7Cu (SAC) solder on the nickel (Ni) substrate electrodeposited on polycrystalline copper (Cu) sheets. The Mo nanoparticles were characterized by transmission electron microscopy (TEM) and X-ray diffractometer (XRD). The composite solder pastes were prepared by manual mixing of Mo nanopartic1es with the SAC solder paste. Ni layer was electrodeposited on polycrystalline Cu substrate by using the Watts bath. The solder paste was placed on the substrate by following the Japanese Industrial Standard (nS) and reflowed up to six times at 250°C for 45 seconds. After first reflow, elemental compositions of the nanocomposite solders were analyzed by inductively coupled plasma-optical emission spectrometer (ICP-OES). The spreading rate and wetting angle of the solder were determined after first reflow. Microstructural investigations at the solder joints were carried out by using high resolution field emission scanning electron microscope (FESEM) and energy dispersive X-ray (EDX). Results reveal that after reflow only a fraction of Mo nanoparticles were retained inside the solder matrix. Mo nanoparticles are effective in suppressing the growth of total IMC layer and scallops during reflow. The retardation of IMC thickness and scallop diameter is suggested due to the discrete particle effect of Me nanoparticles.
Keywords
Nanoparticles, x-ray, energy, polycrystalline copper, field emission scanning electron microscope (FESEM), solder matrix
Divisions
fac_eng
Event Title
1st International Conference on the Science & Engineering of Materials
Event Location
Sunway Putra Hotel, Kuala Lumpur, Malaysia
Event Dates
13-14 November 2013
Event Type
conference