Die attach properties of Zn-Al-Mg-Ga based high-temperature lead-free solder on Cu lead-frame
Document Type
Article
Publication Date
1-1-2012
Abstract
Several candidate alloys have been suggested as high-temperature lead-free solder for Si die attachment by different researchers. Among them, Zn-Al based alloys have proper melting range and excellent thermal/electrical properties. In this study, Zn-Al-Mg-Ga solder wire was used to attach Ti/Ni/Ag metallized Si die on Cu lead-frame in an automatic die attach machine. Die attachment was performed in a forming gas environment at temperature ranging from 370 to 400 A degrees C. At the interface with Cu lead-frame, CuZn(4), Cu(5)Zn(8) and CuZn intermetallic compound (IMC) layers were formed. At the interface with Si, Al(3)Ni(2) IMC formed when 200 nm Ag layer was used at the die back and AgZn and AgZn(3) IMC layers when the Ag layer was 2,000 nm thick. Microstructure of the bulk solder consists of mainly two phases: one with a brighter contrast (about 80.9 wt Zn) and the other one is a mixture of light (about 73.7 wt Zn) and dark phases (about 45 wt Al). Zn-Al-Mg-Ga solder wetted well on Cu lead-frame, covered entire die area and flowed in all directions under the Si die. Less than 10 voids were found in the die attach samples at die attach temperatures of 380 and 390 A degrees C. Die shear strength was found within the acceptable limit (21.8-29.4 MPa) for all the die attach temperatures. Die shear strength of standard Pb-Sn solder was also measured for comparison and was found to be 29.3 MPa. In electrical test, maximum deviation of output voltage after 1,000 thermal cycles was found 12.1.
Keywords
pb-free solders sn-ag-cu interfacial reaction alloys microstructures bumps
Divisions
fac_eng
Publication Title
Journal of Materials Science: Materials in Electronics
Volume
23
Issue
1
Publisher
Springer
Additional Information
Haque, A. Lim, B. H. Haseeb, A. S. M. A. Masjuki, H. H.